Properties

Standard

Results

Test Methods

Melt Flow Rate MFR(5kg), g/10min

0.28±0.05

0.27

GB/T 3682.1-2018

Density ρ , g/cm3

0.9600±0.0040

0.9608

GB/T 1033.2-2010

Tensile Properties:

Tensile Elastic Modulus,MPa

≥ 860

960

GB/T 1040.2-2006

Tensile Stress at Yield,MPa

≥ 23.0

23.4

Tensile Stress at Break ,%

≥ 5.2*10²

> 600

Flexural Modulus Ef, MPa

As report

1.18E±03

GB/T 9341-2008

Simply Supported Beam Notched Impact Strength acA (23°C), kJ/m²

≥ 15

23

GB/T 1043.1-2008

Load Deflection Temperature Tf 0.45, °C

≥ 60

78

GB/T 1634.2-2019

Oxidative Induction Time 0IT (210°C, A1) , min

≥ 20.0

39.8

GB/T 19466.6-2009

Volatile Content, mg/kg

≤ 350

164

GB/T 15558.1-2015

Carbon Black Content, mg/kg

2.0~2.5

2.2

Q/310116000123C025-2020

Carbon Black Dispersion, grade

≤ 3

0.9

GB/T 18251-2019

Hydrostatic Pressure Strength (80°C, 1000h)

No rupture, no leakage (5.4MPa)

No rupture, no leakage (5.4MPa)

GB/T 6111-2018

Resistant to Slow Crack Growth (80°C, 500h)

No rupture, no leakage(0.92MPa)

No rupture, no leakage(0.92MPa)

GB/T 18476-2019

Resistant to Rapid Crack Propaga-tion (RCP) (S4 test, 0°C), MPa

pc, S4≥MOP/2.4-0.072

> 1.0

GB/T 19280

Gas Component Resistance test, (80°C, ring stress 2 MPa) , h

≥20

> 20

GB/T 15558.1-2015

Weldability (butt fusion tensile strength)

Toughness: pass, brittleness: fail

Toughness: pass

GB/T 15558.1-2015